INTERNATIONAL STANDARD ISO 4545-3
Metallic materials — Knoop hardness test —
Part 3:
Calibration of reference blocks
ISO 4545 consists of the following parts, under the general title Metallic materials —— Knoop hardness test:
ISO 4545-1:2005, Metallic materials — Knoop hardness test — Part 1: Test method
ISO 4545-2, Metallic materials — Knoop hardness test — Part 2: Verification and calibration of testing machines
ISO 4545-3:2005, Metallic materials — Knoop hardness test — Part 3: Calibration of reference blocks
ISO 4545-4, Metallic materials — Knoop hardness test — Part 4: Table of hardness values
標準狀態(tài)：已作廢
替代情況：被 ISO 4545-3：2017替代
Contents
Foreword
1. Scope
2 Normative references
3 Manufacture of the block
4 Calibration machine
5 Calibration procedure
6 Number of indentations
7 Uniformity of hardness
8 Marking
9 Validity
Annex A (informative) Adjustment of Kohler illumination systems
Annex B (informative) Uncertainty of measurement of hardness-reference blocks
Bibliography
1 Scope
This part of ISO 4545 specifies the method for the calibration of reference blocks to be used for the indirect verification of Knoop hardness testing machines as specified in ISO 4545-2.
The method is applicable only for indentations with long diagonals W 0,020 mm.
2 Normative references
The following referenced documents are indispensable for the application of this document. For dated references, only the edition cited applies. For undated references, the latest edition of the referenced document (including any amendments) applies.
ISO 376:2004, Metallic materials — Calibration of force-proving instruments used for the verification of uniaxial testing machines
ISO 4287:1997, Geometrical Product Specifications (GPS) — Surface texture: Profile method — Terms, definitions and surface texture parameters
ISO 4545-1:2005, Metallic materials — Knoop hardness test — Part 1: Test method
ISO 4545-2, Metallic materials — Knoop hardness test — Part 2: Verification and calibration of testing machines
相關標準
國家標準GB/T 18449.3-2012 《金屬材料 努氏硬度試驗 第3部分：標準硬度塊的標定》
本標準使用重新起草法修改采用國際標準ISO4545-3:2005《金屬材料 努氏硬度試驗 第3部分:標準硬度塊的標定》(第二版),在文本結構和技術內(nèi)容方面與ISO4545-3:2005一致。
本標準與ISO4545-3:2005的技術性差異及其原因如下:
——刪除了ISO4545-3:2005的前言,重新編寫了前言;
——關于規(guī)范性引用文件,本部分做了具有技術性差異的調整,以適應我國的技術條件,調整的內(nèi)容集中反映在第2章“規(guī)范性引用文件”中,具體調整如下:
● 用等同采用國際標準的GB/T3505代替ISO4287(見3.6);
● 用等同采用國際標準的GB/T13634代替ISO376(見4.4);
● 用修改采用國際標準的GB/T18449.1—2009代替ISO4545-1:2005(見4.5b)﹑第5章和附錄B);
● 用修改采用國際標準的GB/T18449.2—2012代替ISO4545-2:2005(見第1章、4.1﹑附錄B的B.1);
——將既不可能是誤差也不可能是不確定度的不合實際的指標0.02μm 修改成最低分辨力為0.05μm(見4.6);
——國際標準ISO4545-3:2005原文中標準硬度塊的均勻度符號為“U”,易與測量不確定度的符號混淆,本部分用符號“J”表示見7.1和表1);
——刪除了參考文獻。
本標準與ISO4545-3:2005相比存在技術性差異,這些差異涉及的條款已通過在其外側頁邊空白位置的垂直單線(∣)進行了標示。
本標準還做了如下編輯性修改:
——用“本部分”代替“ISO4545的本部分”;
——用中文的小數(shù)點符號“.”代替英文的小數(shù)點符號“,”。
在線閱讀 免費下載